物理性能額定值單位制測試方法比重1.04g/cm3ASTM D792熔流率（熔體流動速率） (220°C/10.0 kg)23g/10 minASTM D1238收縮率 - 流動 (3.20 mm)0.40 到 0.70%ASTM D955Dimensio
nal Stability0.0%ASTM D1042硬度額定值單位制測試方法洛氏硬度 (R 級)110ASTM D785機械性能額定值單位制測試方法拉伸模量 1(3.20 mm)2220MPaASTM D638抗張強度 2(屈服, 3.20 mm)51.0MPaASTM D638伸長率 3(斷裂, 3.20 mm)30%ASTM D638彎曲模量 4(3.20 mm)2750MPaASTM D790彎曲強度 5(3.20 mm)78.5MPaASTM D790沖擊性能額定值單位制測試方法懸壁梁缺口沖擊強度ASTM D256 -30°C, 3.20 mm78J/mASTM D256 -30°C, 6.40 mm78J/mASTM D256 23°C, 3.20 mm230J/mASTM D256 23°C, 6.40 mm200J/mASTM D256熱性能額定值單位制測試方法載荷下熱變形溫度ASTM D648 0.45 MPa, 未退火, 6.40 mm90.0°CASTM D648 1.8 MPa, 未退火, 6.40 mm86.0°CASTM D648維卡軟化溫度94.0°CASTM D1525RTI ElecUL 746 1.50 mm95.0°CUL 746 3.00 mm100°CUL 746RTI ImpUL 746 1.50 mm95.0°CUL 746 3.00 mm100°CUL 746RTIUL 746 1.50 mm95.0°CUL 746 3.00 mm100°C